• Cerakote DFL-200 Dry Film Lubricant Main
  • Cerakote PFAS-Free Logo
  • Cerakote DFL-200 Dry Film Lubricant YouTube Color Sample
  • Cerakote DFL-200 Dry Film Lubricant Example
  • Cerakote DFL-200 Dry Film Lubricant Friction Graph
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample
  • Cerakote DFL-200 Dry Film Lubricant Sample

CERAKOTE

DFL-200 | Dry Film Lubricant Coating

€39,00
€39,00
€330,51 l
Shipping will be calculated at checkout

The prices include import duties and handling, but exclude the VAT applicable in your country.

  • American Express
  • Apple Pay
  • EPS
  • Google Pay
  • Maestro
  • Mastercard
  • PayPal
  • Union Pay
  • Visa
  • Official Distributor
  • Worldwide Sale & Shipping
  • 1-5 Days Express Shipping

Documents

Safety Data Sheet
Application Guide

Questions about the product?

We are happy to help.

  • Low Friction
  • PFAS-free

Cerakote DFL-200 (Dry Film Lubricant) is a PFAS-free, self-lubricating sliding coating that was developed as the first of its kind on the market for extreme durability and low friction in highly demanding environments. Thanks to advanced solid lubricants, it offers superior efficiency, abrasion resistance, and complies with REACH/RoHS regulations – all without fluoropolymers. The coating is easy to apply, cures quickly (15 minutes), and can be applied directly to the substrate – no primer or topcoat is required.

This coating is ideal for applications in aerospace, defense, automotive, and other industries. It cures quickly at low temperatures, integrates easily into any production process, and outperforms conventional alternatives like Molykote®, Teflon®, and Xylan®.

  • Extremely low friction for higher efficiency
  • Over 40% more slippery than Teflon
  • Excellent wear resistance under high load
  • PFAS-free
  • Fast curing at low temperatures for optimized production

Note: The unique properties of our patented dry film lubricant coating reduce friction and wear over the long term. The outermost layer of the coating is designed as a “sacrificial lubricant film.” This creates an ultra-thin, low-friction layer on the contact surface that ensures smooth operation. A small amount of this material may be noticeable during initial handling. This is normal and confirms the coating’s proper function.

This product is supplied with the hardener F-100 and requires a 325-mesh screen (SE-275).

Heat resistance
Chemical resistance
Corrosion protection
UV protection

Technical Data

Filter sieve

325 (Artikel SE-277)

Drying

Oven Curing

Drying Plan

15 minutes in the oven at 120°C

Layer thickness

6.5-19 μm

Gloss Level

7 GU

Density

1.31 g/ml

Proportion of solid components

23%

Viscosity

6 cP

Hardness Grade Gouge (ASTM D3363)

9H

Scratch Hardness (ASTM D3363)

6H

Crosscut Adhesion (ASTM D3359)

 -

Flexibility (Mandrel Bend ASTM D522)

100%

Impact Performance Direct/Indirect (ASTM D2794)

18.08 Nm / 18.08 Nm

Color Stability (max. Temperature)

up to 200°C

Temperature Stability (max.)

up to 760°C

Testing procedures

All results are based on blasted steel coated with the recommended film thickness and cured according to the recommended curing cycle.

Gloss levels are measured at a 60° angle. Deviations from the recommended conditions lead to different results. Gloss is influenced by the quality of pretreatment and the spraying technique.

Viscosity measured under ambient conditions (air temperature, relative humidity) at the time of manufacture.

Recommended curing temperature:

  • Please refer to the curing cycle specifications provided for each Cerakote product.

The maximum temperature is the temperature up to which the paint or coating remains stable.

Chemical resistance testing: The results refer to color changes according to the CIE76 formula. The results range from:

  • Excellent: ∆E change <2.5 (★★★★)
  • Good: ∆E change <3.0 (★★★☆)
  • Satisfactory: ∆E change <3.5 (★★☆☆)
  • Poor: ∆E change <4.0 (★☆☆☆)

The test parameters are as follows:

  • Hardness or pencil hardness tests are measured from soft to hard as follows: 9B, 8B, 7B, 6B, 5B, 4B, 3B, 2B, B, HB, F, H, 2H, 3H, 4H, 5H, 6H, 7H, 8H, 9H. 9H is the highest hardness level.
  • SG-100 only: Hardness test Method A — An X-cut is made through the coating down to the substrate; a self-adhesive tape is applied over the cut and then removed. Adhesion is qualitatively rated on a scale from 0 to 5.
  • Adhesion is measured on a scale from 0B, 1B, 2B, 3B, 4B, 5B, with 5B being the highest achievable rating.
  • Flexibility or bend test on a conical mandrel: “100% resistance” is the highest achievable rating and means the coating showed no cracks or flaking.
  • Impact resistance (direct/indirect) is measured on a scale from 0 Nm to 18.08 Nm, with 18.08 Nm being the highest achievable rating.
DFL-200 | Dry Film Lubricant Coating

€39,00

In-house production

Call us or send us an email if you are interested in implementing Cerakote coating solutions in your company. We are happy to advise you and provide you with all the necessary information.

Outsourcing

If you have your parts manufactured or externally coated by a manufacturer, ask them about Cerakote options for your parts. If they do not offer Cerakote coating, feel free to contact us. We are happy to connect you with one of our certified coaters across Europe.

Call us

If you have any questions or are unsure whether Cerakote is the right application for you, just call us at +49(0)4106-6414121 or send us an email at info@pbncoatings.de.