• Cerakote C-110 Micro Slick Dry Film Lubricant Low Friction Coating Main
  • Cerakote C-110 Micro Slick Dry Film Lubricant Low Friction Coating YouTube Color Sample
  • Cerakote C-110 Micro Slick Dry Film Lubricant Low Friction Coating Customer Sample
  • Cerakote Application Guide - Coating Pistons with Cerakote Piston Coat and Micro Slick YouTube Video
  • Cerakote C-110 Micro Slick Dry Film Lubricant Low Friction Coating Customer Sample
  • Cerakote C-110 Micro Slick Dry Film Lubricant Low Friction Coating Customer Sample
  • Cerakote C-110 Micro Slick Dry Film Lubricant Low Friction Coating Customer Sample

CERAKOTE

C-110 | Micro Slick Dry Film Lubricant (Air Cure)

€39,00
€39,00
€330,51 l
Shipping will be calculated at checkout

The prices include import duties and handling, but exclude the VAT applicable in your country.

  • American Express
  • Apple Pay
  • EPS
  • Google Pay
  • Maestro
  • Mastercard
  • PayPal
  • Union Pay
  • Visa
  • Official Distributor
  • Worldwide Sale & Shipping
  • 1-5 Days Express Shipping

Documents

Safety Data Sheet
Application Guide

Questions about the product?

We are happy to help.

  • Low Friction
  • PFAS-free

Cerakote C-110 Micro Slick Dry Film Lubricant is a PFAS-free, self-lubricating dry film coating that cures in air and appears blue-gray.

Cerakote C-110 Micro Slick Dry Film Lubricant reduces friction of moving parts and is simultaneously oil-repellent. It is used to reduce friction on various internal engine components such as piston skirts, valve stems, and the underside of valve covers. It is also applied to firearm components like bolts and bolt carriers.

The Cerakote ceramic coatings from the C-Series are extremely heat resistant (up to 1000°C) and set new standards in the industry for high-temperature coatings. Additionally, the Cerakote C-Series is very durable, UV-resistant, and also resistant to most solvents and chemicals.

The C-Series includes air-drying, ready-to-spray ceramic coatings based on a unique ceramic technology that ensures flexibility, impressive wear resistance, and long-lasting performance.

NOTE: No hardener is required for this product. This color requires a 325-mesh screen (SE-277).

Heat resistance
Chemical resistance
Corrosion protection
UV protection

Technical Data

Filter sieve

325 (Artikel SE-277)

Drying

Air Curing

Drying Plan

45-60 min. tack free / 5 days 100% full cure

Layer thickness

25 µm

Gloss Level

6 GD

Density

1.36 g/ml

Proportion of solid components

23%

Viscosity

9 cP

Hardness Grade Gouge (ASTM D3363)

9H

Scratch Hardness (ASTM D3363)

9H

Crosscut Adhesion (ASTM D3359)

5B

Flexibility (Mandrel Bend ASTM D522)

99%

Impact Performance Direct/Indirect (ASTM D2794)

6.78 Nm / 6.78 Nm

Color Stability (max. Temperature)

up to 150°C

Temperature Stability (max.)

up to 1000°C

Testing procedures

All results are based on blasted steel coated with the recommended film thickness and cured according to the recommended curing cycle.

Gloss levels are measured at a 60° angle. Deviations from the recommended conditions lead to different results. Gloss is influenced by the quality of pretreatment and the spraying technique.

Viscosity measured under ambient conditions (air temperature, relative humidity) at the time of manufacture.

Recommended curing temperature:

  • Please refer to the curing cycle specifications provided for each Cerakote product.

The maximum temperature is the temperature up to which the paint or coating remains stable.

Chemical resistance testing: The results refer to color changes according to the CIE76 formula. The results range from:

  • Excellent: ∆E change <2.5 (★★★★)
  • Good: ∆E change <3.0 (★★★☆)
  • Satisfactory: ∆E change <3.5 (★★☆☆)
  • Poor: ∆E change <4.0 (★☆☆☆)

The test parameters are as follows:

  • Hardness or pencil hardness tests are measured from soft to hard as follows: 9B, 8B, 7B, 6B, 5B, 4B, 3B, 2B, B, HB, F, H, 2H, 3H, 4H, 5H, 6H, 7H, 8H, 9H. 9H is the highest hardness level.
  • SG-100 only: Hardness test Method A — An X-cut is made through the coating down to the substrate; a self-adhesive tape is applied over the cut and then removed. Adhesion is qualitatively rated on a scale from 0 to 5.
  • Adhesion is measured on a scale from 0B, 1B, 2B, 3B, 4B, 5B, with 5B being the highest achievable rating.
  • Flexibility or bend test on a conical mandrel: “100% resistance” is the highest achievable rating and means the coating showed no cracks or flaking.
  • Impact resistance (direct/indirect) is measured on a scale from 0 Nm to 18.08 Nm, with 18.08 Nm being the highest achievable rating.
C-110 | Micro Slick Dry Film Lubricant (Air Cure)

€39,00

In-house production

Call us or send us an email if you are interested in implementing Cerakote coating solutions in your company. We are happy to advise you and provide you with all the necessary information.

Outsourcing

If you have your parts manufactured or externally coated by a manufacturer, ask them about Cerakote options for your parts. If they do not offer Cerakote coating, feel free to contact us. We are happy to connect you with one of our certified coaters across Europe.

Call us

If you have any questions or are unsure whether Cerakote is the right application for you, just call us at +49(0)4106-6414121 or send us an email at info@pbncoatings.de.